Title: Corrosion Behaviour of the As-Cast and Heat-Treated Za27 Alloy
Authors: Bobic, Biljana
Mitrovic, Slobodan
Babic, Miroslav
Vencl, Aleksandar
Bobic, Ilija
Issue Date: 2011
Abstract: Corrosion behaviour of the as-cast and heat-treated ZA27 alloy was examined. The alloy was prepared by conventional melting and casting route and then thermally processed by applying T4 heat treatment regime (solutionizing at 370 􀁱C for 3 hours followed by water quenching and natural aging). Corrosion rate of the as-cast and heat-treated ZA27 alloy was determined in 3.5 wt. % NaCl solution through immersion test using both weight loss method and polarization resistance measurements. It was shown that applied thermal treatment resulted in increased ductility of the heat-treatedalloy and had a small beneficial effect on the corrosion resistance of ZA27 alloy.
URI: https://scidar.kg.ac.rs/handle/123456789/17121
Type: conferenceObject
Appears in Collections:Faculty of Engineering, Kragujevac

Page views(s)

409

Downloads(s)

21

Files in This Item:
File Description SizeFormat 
Serbiatrib11_091-097.pdf818.41 kBAdobe PDFThumbnail
View/Open


This item is licensed under a Creative Commons License Creative Commons