Назив: Microstructure and magnetic properties of electrodeposited Ni<inf>85.8</inf>Fe<inf>10.6</inf>W<inf>1.4</inf>Cu<inf>2.2</inf> alloy powder
Аутори: Spasojevic, Miroslav
Gospavić D.
Spasojevic, Milica
Датум издавања: 2016
Сажетак: © 2016 The Electrochemical Society. All rights reserved. Nanostructured 85.8 wt%Ni-10.6 wt%Fe-1.4 wt%W-2.2 wt%Cu alloy powder was deposited from an ammonium citrate bath at a current density of 600 mAcm-2. A cathodic polarization curve was recorded, and the current efficiency of the alloy was determined as a function of current density. The deposition of the alloy at current densities up to 400 mAcm-2 is an activation-controlled process. At higher densities, diffusion control is attained. At potentials more positive than -0.90 V, hydrogen evolution from NH4+ and (HCit)3- ions occurs in parallel with the alloy deposition. XRD analysis revealed an amorphous matrix embedded with nanocrystals of the FCC phase of the solid solution of iron, tungsten and copper in nickel. SEM micrographs showed the formation of two shapes of particles: large cauliflower-like particles and small dendritic particles with a large number of secondary and higher-order branches. The annealing of the as-deposited powder causes structural changes which consequently affect its magnetic properties. In the temperature range of 150°C-460°C, structural relaxation takes place, involving short-range ordering and an increase in the relative magnetic permeability of the cooled sample. At temperatures above 460°C, amorphous matrix crystallization and crystalline grain growth of the FCC solid solution occur, resulting in a decrease in the magnetic permeability of the powder.
URI: https://scidar.kg.ac.rs/handle/123456789/11867
Тип: article
DOI: 10.1149/2.1131614jes
ISSN: 0013-4651
SCOPUS: 2-s2.0-85000949362
Налази се у колекцијама:Faculty of Agronomy, Čačak

Број прегледа

149

Број преузимања

5

Датотеке у овој ставци:
Датотека Опис ВеличинаФормат 
PaperMissing.pdf
  Ограничен приступ
29.86 kBAdobe PDFСличица
Погледајте


Ставке на SCIDAR-у су заштићене ауторским правима, са свим правима задржаним, осим ако није другачије назначено.