Назив: Morphological, microstructural and magnetic characteristics of electrodeposited Ni-Fe-W-Cu alloy powders
Аутори: Spasojevic M.
Randjić, Siniša
Maricic, Aleksa
Trišović, Tomislav
Spasojevic M.
Часопис: Science of Sintering
Датум издавања: 1-јан-2020
Сажетак: © 2020 Authors. Published by association for ETRAN Society. Nanostructured Ni-Fe-W-Cu alloy powders were electrodeposited from an alkaline ammonium citrate solution on a titanium cathode. Powder particles were dendrite- and cauliflower-shaped. The dendritic particles had a high density of branches made up of interconnected globules. XRD analysis showed that the powder contained an amorphous matrix and FCC nanocrystals of the solid solution of Fe, W and Cu in Ni. As the deposition current density increased, the mean nanocrystal size decreased, and the mean value of internal microstrain and the total weight percent of Fe and Ni in the alloy increased. The powders deposited at higher current densities exhibited higher magnetization. During annealing at temperatures up to 460 °C, the powders underwent short-range ordering, which caused an increase in magnetization, whereas at temperatures above 460 °C, the magnetization decreased due to the formation of large FCC crystalline grains.
URI: https://scidar.kg.ac.rs/handle/123456789/10713
Тип: journal article
DOI: 10.2298/SOS2001109S
ISSN: 0350820X
SCOPUS: 85083971442
Налази се у колекцијама:Faculty of Agronomy, Čačak
Faculty of Technical Sciences, Čačak

Број прегледа

109

Број преузимања

2

Датотеке у овој ставци:
Датотека Опис ВеличинаФормат 
10.2298-SOS2001109S.pdf1.15 MBAdobe PDFСличица
Погледајте


Ставке на SCIDAR-у су заштићене ауторским правима, са свим правима задржаним, осим ако није другачије назначено.