Title: Advantages of combined sintering compared to conventional sintering of mechanically activated magnesium titanate
Authors: Filipović, Suzana
Obradovic, Nina
Pavlović, Vladimir
Kosanović, Darko
Mitric M.
Mitrovic, Nebojsa
Pouchly V.
Kachlík, Martin
Maca K.
Issue Date: 2014
Abstract: © 2014 Science of Sintering. In this article, the advantages of combined sintering in comparison with the conventional one, of mechanically activated magnesium titanate ceramic were investigated. The stoichiometric mixtures of MgO and TiO2 were mechano-chemically activated for 0, 10, 40, 80 and 160 minutes by ball milling and then isostatically pressed (CIP) to form green bodies. Conventional sintering was realized by heating up to 1400oC and hold for 30 minutes in air atmosphere. Resulting ceramic samples with closed porosity were post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 128oC/3h in argon atmosphere with a pressure of 200 MPa. The best results were observed in the case of samples post-sintered by HIP, when single-phase MgTiO3 samples with relative density of 96% were prepared.
Type: article
DOI: 10.2298/SOS1403283F
ISSN: 0350-820X
SCOPUS: 2-s2.0-84920937736
Appears in Collections:Faculty of Technical Sciences, Čačak

Page views(s)




Files in This Item:
File Description SizeFormat 
  Restricted Access
29.86 kBAdobe PDFThumbnail

Items in SCIDAR are protected by copyright, with all rights reserved, unless otherwise indicated.