Title: The influence of corrosion on the microstructure of thermally treated ZA27/SICP composites
Authors: Bobic, Biljana
Vencl, Aleksandar
Babic, Miroslav
Mitrovic, Slobodan
Bobic, Ilija
Issue Date: 2013
Abstract: The influence of corrosion on the microstructure of ZA27/SiCp composites was examined. The composites were produced by compo casting technique and then subjected to the thermal treatment (T4 regime). Microstructural examinations were performed after 30-day exposure of thermally treated composites in the sodium-chloride solution. Corrosion processes have occurred in the composite matrix. Corrosion did not affect SiC particles in the composites. The local progress of corrosion in depth of the composite matrix was noticed in micro-cracks. Corrosion resistance of ZA27/SiCp composites was evaluated based on the mass loss of composite samples during the immersion test. It was found that corrosion resistance of the composites decreased with increase in content of SiC particles. The applied thermal treatment had a negative influence on the corrosion resistance of ZA27/SiCp composites.
URI: https://scidar.kg.ac.rs/handle/123456789/17092
Type: conferenceObject
Appears in Collections:Faculty of Engineering, Kragujevac

Page views(s)

324

Downloads(s)

11

Files in This Item:
File Description SizeFormat 
Serbiatrib13 106-112.pdf2.05 MBAdobe PDFThumbnail
View/Open


This item is licensed under a Creative Commons License Creative Commons