Tribological Behaviour of Hypereutectic Al-Si Composites: A Multi-Response Optimisation Approach with ANN and Taguchi Grey Method

Abstract

An optimisation model for small datasets was applied to thixocasted/compocasted compos- ites and hybrid composites with hypereutectic Al-18Si base alloys. Composites were produced with the addition of Al2O3 (36 μm/25 nm) or SiC (40 μm) particles. Based on the design of experiment, tribological tests were performed on the tribometer with block-on-disc contact geometry for normal loads of 100 and 200 N, a sliding speed of 0.5 m/s, and a sliding distance of 1000 m. For the prediction of the tribological behaviour of composites, artificial neural networks (ANNs) were used. Three inputs were considered for ANN training: type of reinforcement (base alloy, Al2O3 and SiC), amount of Al2O3 nano-reinforcement (0 and 0.5 wt.%), and load (100 and 200 N). Various ANNs were applied, and the best ANN for wear rate (WR), with an overall regression coefficient of 0.99484, was a network with architecture 3-15-1 and a logsig (logarithmic sigmoid) transfer function. For coefficient of friction (CoF), the best ANN was the one with architecture 3-6-1 and a tansig (hyperbolic tangent sigmoid) transfer function and had an overall regression coefficient of 0.93096. To investigate the potential of ANN for the prediction of two outputs simultaneously, an ANN was trained, and the best results were from network 3-5-2 with a logsig transfer function and overall regression coefficient of 0.99776, but the predicted values for CoF in this case did not show good correlation with experimental results. After the selection of the best ANNs, the Taguchi grey multi-response optimisation of WR and CoF was performed for the same combination of factors as the ANNs. For optimal WR and CoF, the com- bination of factors was as follows: composite with 3 wt.% Al2O3 micro-reinforcement, 0.5 wt.% Al2O3 nano-reinforcement, and a load of 100 N. The results show that developed ANN, the Taguchi method, and the Taguchi grey method can, with high reliability, be used for the optimisation of wear rate and coefficient of friction of hypereutectic Al-Si composites. Microstructural investigations of worn surfaces were performed, and the wear mechanism for all tested materials was light abrasion and adhesion. The findings from this research can contribute to the future development of hypereutectic Al-Si composites.